1. Product Introduction

Lydorflam 5203 is a halogen-free flame retardant for nylon and polyester materials, primarily functioning through char formation and gas phase flame retardancy mechanisms. The product features high thermal stability and low addition amounts, making it suitable for flame retardant modification of glass fiber reinforced nylon products and polyester materials, achieving UL-94 V0 level flame retardancy without dripping. The product has excellent overall performance, outstanding water resistance, and excellent electrical properties, making it an ideal substitute for brominated antimony flame retardants.

2. Product Specifications

3. Recommended Dosage

4. Product Characteristics

1. Fully control the moisture content of raw materials to minimize the impact of moisture on product performance.

2.Ensure even dispersion, and add dispersant as needed to improve material flame retardancy efficiency.

5. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

Four, Thermogravimetric Analysis

Image uploading.....

Image upload failed...

Five, Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product Introduction

Lydorflam 5223 is a halogen-free flame retardant applied to nylon materials, mainly functioning through char formation and gas-phase flame retardant mechanisms. The product has high thermal stability, no migration, no precipitation, and low addition amount characteristics, making it applicable for flame retardancy in pure nylon and glass fiber reinforced products, achieving UL-94 V0 level flame retardancy without dripping. The product has excellent comprehensive performance, outstanding water resistance, and excellent electrical properties, making it an ideal substitute for brominated antimony flame retardants.

II. Product Specifications

III. Recommended Dosage

*Material mechanical properties are typical values tested in our laboratory, for reference only, not as a quality commitment

IV. Product Characteristics

1.5223 can improve the impact resistance of nylon materials;

2. Use immediately after opening, if left for a long time, before use90℃ drying2hours;

3.The flame retardant performance of the product is not affected by commonly used antioxidants, lubricants, carbon black, and other additives;

4.The flame retardant performance of the product is not affected by a small amount of inorganic fillers (addition amount ≤5%), such as talcum powder/Sillimanite/Effect of Barium Sulfate;

5.If toughening agents are added, the amount of flame retardants needs to be increased accordingly;

6.Product is resistant to high temperature and high humidity, dual85Test (85℃,85%RH）Passed168No precipitation after hours of testing, no impact on flame retardant performance;

7.This product does not produce dust and is easy to discharge and process.

V. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product Introduction

Lydorflam 5223A A halogen-free flame retardant for nylon materials, mainly functioning through char formation and gas-phase flame retardant mechanisms. The product has high thermal stability, no migration, no precipitation, and low addition amount characteristics, and can be applied to pure nylon and glass fiber reinforced products for flame retardancy, achieving UL-94 V0 level flame retardant performance without dripping. The product has excellent comprehensive performance, outstanding water resistance, and excellent electrical properties, making it an ideal substitute for brominated antimony flame retardants.

II. Product Specifications

III. Recommended Usage

*The mechanical properties of the material are typical values tested in our laboratory, for reference only, and do not constitute a quality commitment

IV. Product Characteristics

1. Use immediately after opening, if left for a long time,90℃ Drying2hours;

2.The flame retardant performance of the product is not affected by commonly used antioxidants, lubricants, carbon black, and other additives;

3.The flame retardant performance of the product is not affected by a small amount of inorganic fillers (addition amount ≤5%），such as talcum powder/Talc/the influence of barium sulfate;

4.If adding toughening agents, the addition amount of flame retardants needs to be increased accordingly;

5.The product is resistant to high temperature and high humidity, double85Test (85℃,85%RH）Pass168No precipitation after hours of testing, with no impact on flame retardant performance;

6.This product does not generate dust and is easy to discharge and process.

V. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product Introduction

Lydorflam 5007 is a new type of phosphorus, nitrogen, and bromine flame retardant suitable for polyolefins. It achieves flame retardant effects through mechanisms of expansion, carbonization, and thermal insulation, meeting the GWIT850℃ glowing wire requirements. Polyolefins flame-retarded with Lydorflam 5007 have characteristics such as low density and low smoke generation, and can successfully pass UL746C and glowing wire IEC60695-2 standard tests.

II. Product Specifications

Appearance: white powder N content: ≥19%

Whiteness: 94% P content: ≥15%

Particle size: ~10um Bromine content: ≤4%

Density: ~1.8g/cm3 Decomposition temperature: ≥282℃

Moisture: ≤0.5% Water solubility: ≤0.2%

III. Recommended Dosage:

IV. Product Characteristics

1. It has excellent heat resistance, with a decomposition temperature greater than 282℃, and is not prone to black spots.

2. It can provide a wide processing temperature range, and a screen can be added during extrusion and granulation.

3. No exudation, water boil resistant, can meet the 85℃, 168H water boil test.

4. Not affected by color powders, especially not affected by carbon black.

3. The flame retardant works through expansion and carbonization mechanisms, and any inorganic mineral fillers that destroy the flame retardant mechanism will affect the flame retardancy;

4. Choose a reasonable processing temperature to avoid the decomposition of the flame retardant under high temperature conditions; it is recommended that the processing temperature be between 180～190℃, and the screen at the die head should be removed.

V. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

1. Product Introduction

Lydorflam 5009L is a new type of phosphorus-nitrogen halogen-free flame retardant suitable for polyolefins, integrating acid source, carbon source, and gas source to achieve flame retardancy through carbonization and expansion mechanisms. Polyolefins flame-retarded with Lydorflam 5009L do not contain halogen elements or heavy metal elements, and the flame-retardant products have characteristics such as low density and low smoke generation.

2. Product Specifications

Appearance: White powder               Particle size: 10-15μm

Moisture: ≤0.7%                     Decomposition Temperature: ≥265

3. Recommended Dosage

4. Processing Precautions:

1. Lydorflam 5009L has a relatively low bulk density, and the dispersion of the flame retardant plays a key role in the flame retardancy and processability of the product. To achieve better results, it is recommended to add an appropriate amount of dispersant to the formulation system to improve the dispersion and processability of the flame retardant.

2. The bulk density of the flame retardant is relatively low. A suitable resin with a high melt flow index can effectively coat the flame retardant. It is recommended to choose a resin with a medium to high melt flow index as the base material.

3. The flame retardant works through expansion and carbonization mechanisms; any inorganic mineral fillers that disrupt the flame retardant mechanism will affect its performance.

4. Choose a reasonable processing temperature to avoid the decomposition of the flame retardant under high temperatures. It is recommended to process at temperatures between 180 and 190℃, and to remove the screen from the die head.

5. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product introduction

Lydorflam5010 flame retardant is an efficient flame retardant using phosphorus, nitrogen, and bromine as flame retardant elements, applied to polypropylene. It acts through gas phase and condensed phase flame retardant mechanisms, and adding 2% can meet the UL-94 V2 combustion requirements and pass the IEC60695-2 glowing wire test smoothly. Compared with traditional brominated flame retardants, its addition amount is low, does not require additional antimony trioxide, and has characteristics such as no precipitation, water resistance, and non-toxicity.

II. Product specifications

Appearance: white powder Moisture: ≤0.5%

P content: ≥8% Decomposition temperature: > 270℃

Br content: ≤2%

III. Application characteristics

1. No precipitation: No precipitation on the surface after baking at 130℃ for 168H

2. High dielectric property: dielectric strength > 6000V

3. Water resistance: Soaking in 75℃ hot water for 168H, excellent flame retardancy

4. Meets IEC60695-2-13 requirement of 775℃ and IEC60695-2-12 requirement of 850℃

5. Excellent high-temperature thermal aging, performance remains unchanged after 150℃, 2000H thermal aging

6. Can be compounded with different minerals such as talcum powder and barium sulfate for flame retardancy

IV. Processing precautions

1. Due to the small addition ratio, uniform dispersion must be ensured to meet the flame retardant requirements;

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, leading to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170～190 ℃.

V. Packaging and storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product Introduction

Lydorflam 5001 is a new type of phosphorus and nitrogen halogen-free flame retardant suitable for polyolefins. The product exists in a cage-like molecular structure, integrating acid source, carbon source, and gas source, and does not contain APP. It achieves flame retardant effects through expansion, carbonization, and thermal insulation mechanisms. Polyolefins flame-retarded with Lydorflam 5001 do not contain halogen elements or heavy metal elements, and the flame-retardant products have characteristics such as low density and low smoke generation, successfully passing UL746C and glow wire IEC60695-2 standards tests.

II. Product Specifications

Appearance: White powder N content: ≥19%

Whiteness: 93% P content: ≥18%

Particle size: ~10um Solubility: ≤0.2%

Density: ~1.8g/cm3 Decomposition temperature: ≥285℃

Moisture: ≤0.5%

III. Recommended Dosage:

IV. Product Characteristics

1. Excellent heat resistance, decomposition temperature greater than 285℃, not easy to produce black spots

2. Can provide a wide processing temperature range, a screen can be added during extrusion and granulation

3. No precipitation, water boiling resistant, can meet 85℃, 168H boiling water test

4. Can be compounded with talc powder, wollastonite, barium sulfate, glass fiber and other minerals

5. Not affected by color powders, especially not affected by carbon black

V. Processing Precautions

1. Due to the relatively low bulk density of Lydorflam 5001, the dispersion of the flame retardant plays a key role in the flame retardant effect and processing of the product. To achieve better results, it is recommended to add an appropriate amount of dispersant in the formulation system, combined with a strong shear dispersing screw combination to improve the dispersibility and processability of the flame retardant.

2. The bulk density of the flame retardant is relatively low, selecting a suitable melt index resin can effectively coat the flame retardant, it is recommended to choose medium to high melt index resins as the base material.

VI. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product introduction

Lydorflam5014 flame retardant is a flame retardant with phosphorus, nitrogen, and bromine as flame retardant elements, suitable for flame retardant of copolymer PP materials. It acts through gas phase and condensed phase flame retardant mechanisms, and an addition of 2% can meet UL-94 V2 combustion requirements and successfully pass IEC60695-2 glowing wire test and flame test. Compared with traditional brominated flame retardants, its addition amount is low, does not require additional antimony trioxide, and has characteristics such as no precipitation, water resistance, and non-toxicity.

II. Product specifications

Appearance: White powder Moisture: ≤0.5%

P content: ≥25% Decomposition temperature: > 275℃

Br content: ≤2%

III. Application characteristics

1. No precipitation: No precipitation on the surface after baking at 130℃ for 168H

2. High dielectric property: Dielectric strength > 6000V

3. Water resistance: Soaking in 75℃ hot water for 168H, excellent flame retardancy

4. Meets IEC60695-2-13 requirement of 775℃ and IEC60695-2-12 requirement of 850℃

5. Excellent high-temperature thermal aging performance, maintaining good performance after 150℃, 2000H thermal aging

6. Can be compounded with different minerals such as talc powder and barium sulfate for flame retardancy

IV. Processing precautions

1. Due to the small addition ratio, it is necessary to ensure uniform dispersion to meet flame retardant requirements.

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, leading to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170～190 ℃.

V. Packaging and storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

V. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

One, Product Introduction

Lydorflam5107 flame retardant is an efficient flame retardant that uses phosphorus, nitrogen, and bromine as flame retardant elements, applied to polypropylene. It acts as a flame retardant through gas phase and condensed phase mechanisms, and an addition of 2-4% can meet the UL-94 V2 combustion requirements, with an oxygen index of over 26. Compared to traditional brominated flame retardants, its addition amount is low, and there is no need to add antimony trioxide, while also possessing characteristics such as no leaching, water resistance, and non-toxicity.

Two, Product Specifications 

Appearance: white powder Moisture: ≤0.5% 

P content: ≥8% Br content: ≤2%

Particle size D50 ≤15μm

Three, Processing Precautions

1. Due to the small addition ratio, it must be evenly dispersed to meet the flame retardant requirements;

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, which can lead to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170-190 ℃.

Four, Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

One, Product Introduction

Lydorflam5013T flame retardant is a flame retardant that uses phosphorus, nitrogen, and bromine as flame retardant elements, functioning through gas phase and dripping flame retardant mechanisms. Adding 1-4% can meet UL-94 V2, glowing wire GWFI 750℃ test, and needle flame test. Compared to traditional bromine-antimony system flame retardants, it has a lower addition amount, does not require additional antimony trioxide, and possesses characteristics such as no leaching, water resistance, and non-toxicity.

Two, Product Specifications

Appearance: white powder Moisture: ≤0.6%

P content: ≥20% Br content: ≤10%

Three, Application Characteristics 

1. The recommended addition amount is 1-4%, and the specific addition amount should be determined based on the customer's formula;

2. The glowing wire GWFI 750℃ test can be conducted;

3. Barium sulfate, wollastonite, etc. can be used for filling modification (the addition amount of the flame retardant needs to be appropriately increased);

Four, Processing Precautions

1. Due to the small addition ratio, it must be ensured that it is evenly dispersed to meet flame retardant requirements.

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, leading to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170～190℃.

Five, Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.