I. Product introduction

Lydorflam5010 flame retardant is an efficient flame retardant using phosphorus, nitrogen, and bromine as flame retardant elements, applied to polypropylene. It acts through gas phase and condensed phase flame retardant mechanisms, and adding 2% can meet the UL-94 V2 combustion requirements and pass the IEC60695-2 glowing wire test smoothly. Compared with traditional brominated flame retardants, its addition amount is low, does not require additional antimony trioxide, and has characteristics such as no precipitation, water resistance, and non-toxicity.

II. Product specifications

Appearance: white powder Moisture: ≤0.5%

P content: ≥8% Decomposition temperature: > 270℃

Br content: ≤2%

III. Application characteristics

1. No precipitation: No precipitation on the surface after baking at 130℃ for 168H

2. High dielectric property: dielectric strength > 6000V

3. Water resistance: Soaking in 75℃ hot water for 168H, excellent flame retardancy

4. Meets IEC60695-2-13 requirement of 775℃ and IEC60695-2-12 requirement of 850℃

5. Excellent high-temperature thermal aging, performance remains unchanged after 150℃, 2000H thermal aging

6. Can be compounded with different minerals such as talcum powder and barium sulfate for flame retardancy

IV. Processing precautions

1. Due to the small addition ratio, uniform dispersion must be ensured to meet the flame retardant requirements;

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, leading to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170～190 ℃.

V. Packaging and storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

I. Product introduction

Lydorflam5014 flame retardant is a flame retardant with phosphorus, nitrogen, and bromine as flame retardant elements, suitable for flame retardant of copolymer PP materials. It acts through gas phase and condensed phase flame retardant mechanisms, and an addition of 2% can meet UL-94 V2 combustion requirements and successfully pass IEC60695-2 glowing wire test and flame test. Compared with traditional brominated flame retardants, its addition amount is low, does not require additional antimony trioxide, and has characteristics such as no precipitation, water resistance, and non-toxicity.

II. Product specifications

Appearance: White powder Moisture: ≤0.5%

P content: ≥25% Decomposition temperature: > 275℃

Br content: ≤2%

III. Application characteristics

1. No precipitation: No precipitation on the surface after baking at 130℃ for 168H

2. High dielectric property: Dielectric strength > 6000V

3. Water resistance: Soaking in 75℃ hot water for 168H, excellent flame retardancy

4. Meets IEC60695-2-13 requirement of 775℃ and IEC60695-2-12 requirement of 850℃

5. Excellent high-temperature thermal aging performance, maintaining good performance after 150℃, 2000H thermal aging

6. Can be compounded with different minerals such as talc powder and barium sulfate for flame retardancy

IV. Processing precautions

1. Due to the small addition ratio, it is necessary to ensure uniform dispersion to meet flame retardant requirements.

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, leading to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170～190 ℃.

V. Packaging and storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

V. Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

One, Product Introduction

Lydorflam5107 flame retardant is an efficient flame retardant that uses phosphorus, nitrogen, and bromine as flame retardant elements, applied to polypropylene. It acts as a flame retardant through gas phase and condensed phase mechanisms, and an addition of 2-4% can meet the UL-94 V2 combustion requirements, with an oxygen index of over 26. Compared to traditional brominated flame retardants, its addition amount is low, and there is no need to add antimony trioxide, while also possessing characteristics such as no leaching, water resistance, and non-toxicity.

Two, Product Specifications 

Appearance: white powder Moisture: ≤0.5% 

P content: ≥8% Br content: ≤2%

Particle size D50 ≤15μm

Three, Processing Precautions

1. Due to the small addition ratio, it must be evenly dispersed to meet the flame retardant requirements;

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, which can lead to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170-190 ℃.

Four, Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.

One, Product Introduction

Lydorflam5013T flame retardant is a flame retardant that uses phosphorus, nitrogen, and bromine as flame retardant elements, functioning through gas phase and dripping flame retardant mechanisms. Adding 1-4% can meet UL-94 V2, glowing wire GWFI 750℃ test, and needle flame test. Compared to traditional bromine-antimony system flame retardants, it has a lower addition amount, does not require additional antimony trioxide, and possesses characteristics such as no leaching, water resistance, and non-toxicity.

Two, Product Specifications

Appearance: white powder Moisture: ≤0.6%

P content: ≥20% Br content: ≤10%

Three, Application Characteristics 

1. The recommended addition amount is 1-4%, and the specific addition amount should be determined based on the customer's formula;

2. The glowing wire GWFI 750℃ test can be conducted;

3. Barium sulfate, wollastonite, etc. can be used for filling modification (the addition amount of the flame retardant needs to be appropriately increased);

Four, Processing Precautions

1. Due to the small addition ratio, it must be ensured that it is evenly dispersed to meet flame retardant requirements.

2. Equipment must ensure accurate temperature control to avoid local overheating due to inaccurate temperature control, leading to the decomposition of the flame retardant. It is recommended to set the processing temperature range at: 170～190℃.

Five, Packaging and Storage

25Kg/bag, transported as general chemicals, stored in a dry and cool place, avoiding direct sunlight.